310S Stainless Steel Strip Description
310S stainless steel coil has good oxidation resistance, corrosion resistance, acid and alkali resistance due to the high content of nickel (Ni) and chromium (Cr). After increasing the content of carbon in austenitic stainless steel, the strength is improved because of its solid solution strengthening effect. The chemical composition characteristics of austenitic stainless steel are based on chromium and nickel to add molybdenum, tungsten, niobium and titanium, and because of its face-centered cubic structure, it has high strength and creep strength at high temperatures. 310S stainless steel is often used to manufacture boiler, steam turbine, industrial furnace and aviation, petrochemical and other parts of the industry.
Product Parameters
| Product Name | 310S Stainless Steel Strip |
| Type | Steel Coil |
| Thickness | 2.5mm-10.0mm |
| Length | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc. |
| Width | 610mm-2000mm |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. |
| Surface | BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
| Scope of Application | Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging,
Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. |
| Certificate | ISO, SGS, BV, etc. |
| Production Technology | Hot Rolling, Cold Rolling |
| Edge Processing | Edging, Trimming |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
| ≤ 0.08 | ≤1.0 | ≤ 2.0 | 24.0～26.0 | 19.0～22.0 | ≤ 0.03 | ≤ 0.045 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥520 | ≥205 | ≥40 | ≤ 217HB;≤ 95HRB |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
| 9.01 | 200 | 14.4 | 13.8 | 94 |